KetaSpire® KT-851 NL|PEEK|Solvay物性表报告及物性特性介绍,KetaSpire® KT-851 NL|PEEK|Solvay注塑参数详情-塑料物性表查询网

加工/物理特性	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
熔体流动指数(Melt Flow Index)	10	g/10min	ASTM D 1238
温度(Temperature)	400	°C	-
负载(Load)	2.16	kg	-
模具收缩(Mold Shrinkage) (MD)	0.012	mm/mm	ASTM D 955
模具收缩(Mold Shrinkage) (TD)	0.014	mm/mm	ASTM D 955
密度(Density) (73°F)	1300	kg/m³	ASTM D 792
吸水率(Water Absorption) (24hr)	0.1	%	ASTM D 570

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	3850	MPa	ISO 527-1/-2
屈服应力(Yield stress)	95	MPa	ISO 527-1/-2
屈服应变(Yield strain)	4.8	%	ISO 527-1/-2
破坏时应变(Strain at break)	25	%	ISO 527-1/-2
弯曲弹性模量(Flexural modulus) (23°C)	3620	MPa	ISO 178
悬臂梁式冲击切口 (23°C)	7.5	kJ/m²	ISO 180/1A
悬臂梁式冲击无切口(Izod Impact unnotched) (23°C)	N	kJ/m²	ISO 180/1U
ASTM数据(ASTM Data)
拉伸模量(Tensile Modulus)	3600	MPa	ASTM D 638
抗拉强度(Tensile Strength)	96	MPa	ASTM D 638
屈服伸长率(Elongation at Yield)	5.2	%	ASTM D 638
断裂伸长率(Elongation at Break)	25	%	ASTM D 638
抗压强度(Compressive Strength)	121	MPa	ASTM D 695
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	3900	MPa	ASTM D 790
抗弯强度(Flexural Strength)	152	MPa	ASTM D 790
洛氏硬度(Rockwell Hardness)	M 97	-	ASTM D 785
Shore D Hardness	88	-	ASTM D 2240
悬臂梁式冲击切口 (1/8 in)	0.069	kJ/m	ASTM D 256

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
DTUL @ 264 psi	157	°C	ASTM D 648
Glass Transition 温度(Temperature)	150	°C	ASTM E 1356

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
绝缘强度(Dielectric Strength) (Short Time)	200	kV/mm	ASTM D 149
表面电阻率(Surface Resistivity)	>1E15	Ohm	ASTM D 257
体积电阻率(Volume Resistivity)	>1E15	Ohm*cm	ASTM D 257

CharacteristicsProcessingInjection Molding, Profile Extrusion, CoatingDelivery formPellets, Natural ColorSpecial CharacteristicsFlame retardant, High impact or impact modified, Heat stabilized or stable to heatFeaturesDuctile, Fatigue ResistanceChemical ResistanceAcid Resistance, Alkali Resistance, General Chemical Resistance, Oil ResistanceApplicationsAsia Pacific, South and Central America,.