Product TextsVESTAKEEP® 2000 G7	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.2	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	3700	MPa	ISO 527-1/-2
屈服应力(Yield stress)	100	MPa	ISO 527-1/-2
屈服应变(Yield strain)	5	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	30	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	6	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	6	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	340	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	155	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	205	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	310	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	60	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	V-0	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6	mm	IEC 60695-11-10
Oxygen index	38	%	ISO 4589-1/-2

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	2.8	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	2.8	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	50	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	1E15	Ohm	IEC 60093
相比漏电起痕指数(Comparative tracking index)	200	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.5	%	Sim. to ISO 62
密度(Density)	1300	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	370	°C	ISO 294
Injection Molding, mold temperature	180	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294
Injection Molding, pressure at hold	120	MPa	ISO 294

Diagrams25 %The drying time is dependent on theIn practice a drying time of 2 - 3 hours at a temperature of 150 - 160 °C (depen- With the exeption of 25 %The drying time is dependent on theIn practice a drying time of 2 - 3 hours at a temperature of 150 - 160 °C (depen- With the exeption ofISO 1817 Liquid C) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid 4) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid F) (23°C)[/td][/tr][tr][td]Salt solutions[/td][/tr][tr][td] .