Arnitel® PL581|TPC|DSM物性表报告及物性特性介绍,Arnitel® PL581|TPC|DSM注塑参数详情-塑料物性表查询网

Product TextsInjection Molding16

ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	210	MPa	ISO 527-1/-2
屈服应力(Yield stress)	17	MPa	ISO 527-1/-2
屈服应变(Yield strain)	35	%	ISO 527-1/-2
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	N	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	16	kJ/m²	ISO 179/1eA
Stress at 10% elongation	13.2	MPa	ISO 527-1/-2
Stress at 100% elongation	17	MPa	ISO 527-1/-2
破坏时应变(Strain at break) TPE	300	%	ISO 527-1/-2
破坏时应变(Stress at break) TPE	31	MPa	ISO 527-1/-2
抗拉强度(撕裂强度(Tear strength))	125	kN/m	ISO 34-1

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	218	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	100	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	105	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	110	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	110	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6	mm	IEC 60695-11-10

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (1MHz)	4	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	400	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
电气强度(Electric strength)	21	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	600	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	2.5	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.4	%	Sim. to ISO 62
密度(Density)	1240	kg/m³	ISO 1183

CharacteristicsProcessingInjection Molding, Other ExtrusionDelivery formPelletsRegional AvailabilityNorth America, Europe, Asia PacificOther text informationInjection moldingInjection Molding RecommendationsDisclaimerCopyright M-Base .