Hytrel® 6646 NC010|TPC|DuPont物性表报告及物性特性介绍,Hytrel® 6646 NC010|TPC|DuPont注塑参数详情-塑料物性表查询网

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
成型收缩(Molding shrinkage) (parallel)	1.3	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.2	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	290	MPa	ISO 527-1/-2
屈服应力(Yield stress)	20	MPa	ISO 527-1/-2
屈服应变(Yield strain)	30	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	>50	%	ISO 527-1/-2
Tensile creep modulus (1h)	260	MPa	ISO 899-1
Tensile creep modulus (1000h)	190	MPa	ISO 899-1
简支梁冲击强度(Charpy impact strength) (+23°C)	N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	110	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	13	kJ/m²	ISO 179/1eA
Stress at 10% elongation	16	MPa	ISO 527-1/-2
Stress at 100% elongation	20	MPa	ISO 527-1/-2
破坏时应变(Strain at break) TPE	>300	%	ISO 527-1/-2
破坏时应变(Stress at break) TPE	40	MPa	ISO 527-1/-2
Shore D hardness (15s)	61	-	ISO 868

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	211	°C	ISO 11357-1/-3
玻璃化转变温度(Glass transition temperature) (10°C/min)	0	°C	ISO 11357-1/-2
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	45	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	85	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	100	°C	ISO 306
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.0	mm	IEC 60695-11-10
Oxygen index	21	%	ISO 4589-1/-2

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	123	kg/m³	ISO 1183

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density) of melt	1070	kg/m³	-
熔体热导率(Thermal conductivity of melt)	0.15	W/(m K)	-
规格的热容融化(Spec. heat capacity of melt)	2150	J/(kg K)	-
Eff. thermal diffusivity	5.44E-8	m²/s	-
喷射温度(Ejection temperature)	130	°C	-

CharacteristicsProcessingInjection Molding, Film Extrusion, Profile Extrusion, Sheet Extrusion, Other Extrusion, Casting, ThermoformingDelivery formPelletsSpecial CharacteristicsLight stabilized or stable to lightRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSINGEng.Oil, ISP (140°C)

ISO 1817 Liquid C) (23°C)

ISO 1817 Liquid 4) (23°C)

ISO 1817 Liquid F) (23°C)

ISO 1817 Liquid F) (90°C)

ISO 1817 Liquid F) (>90°C)

4 Brake fluid (130°C)