Hytrel® HTR8139BK|TPC|DuPont物性表报告及物性特性介绍,Hytrel® HTR8139BK|TPC|DuPont注塑参数详情-塑料物性表查询网

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	1.9	cm³/10min	ISO 1133
温度(Temperature)	230	°C	ISO 1133
负载(Load)	2.16	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	1.6	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.4	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	55	MPa	ISO 527-1/-2
Stress at 50% strain	10	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	>50	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	N	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	N	kJ/m²	ISO 179/1eA
Stress at 10% elongation	6.9	MPa	ISO 527-1/-2
Stress at 100% elongation	14	MPa	ISO 527-1/-2
Stress at 300% elongation	23	MPa	ISO 527-1/-2
破坏时应变(Strain at break) TPE	300	%	ISO 527-1/-2
破坏时应变(Stress at break) TPE	30	MPa	ISO 527-1/-2
Shore D hardness (15s)	41	-	ISO 868
ASTM数据(ASTM Data)
抗拉强度(Tensile Strength) at Break	28	MPa	ASTM D 638
断裂伸长率(Elongation at Break)	500	%	ASTM D 638
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	86.0002	MPa	ASTM D 790
Shore D Hardness	46	-	ASTM D 2240
悬臂梁式冲击切口 (Low-温度(Temperature))	N	kJ/m	ASTM D 256
温度(Temperature)	-40	°C	ASTM D 256

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	194	°C	ISO 11357-1/-3
玻璃化转变温度(Glass transition temperature) (10°C/min)	-45	°C	ISO 11357-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	60	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	180	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	190	E-6/K	ISO 11359-1/-2
Oxygen index	21	%	ISO 4589-1/-2
ASTM数据(ASTM Data)
热膨胀系数(Coefficient of Thermal Expansion) (MD)	192	E-6/K	ASTM D 696
热膨胀系数(Coefficient of Thermal Expansion) (TD)	176	E-6/K	ASTM D 696
熔化温度(Melting 温度(Temperature))	192	°C	ASTM D 3418

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	4.9	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	4.6	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	50	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	275	E-4	IEC 60250
体积电阻率(Volume resistivity)	4E11	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
电气强度(Electric strength)	19	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	600	-	IEC 60112

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density) of melt	960	kg/m³	-
Eff. thermal diffusivity	5.44E-8	m²/s	-

Diagrams ISO 1817 Liquid C) (23°C)

ISO 1817 Liquid 4) (23°C)

ISO 1817 Liquid F) (23°C)

ISO 1817 Liquid F) (90°C)

ISO 1817 Liquid F) (>90°C)

Salt solutions

4 Brake fluid (130°C)