PP/HF3202/LG化学
- 生产企业： LG化学
①原料描述部分
| 规格级别 | 高抗冲 其它 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | |||
| 备注说明 | |||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.06 | ||
| 成型收缩率 | ASTM D-955 | 0.9-1.3 | % | ||
| 机械性能 | 弯曲模量 | ASTM D-790 | 330 | psi | |
| 拉伸屈服强度 | ASTM D-638 | 4100 | psi | ||
| 拉伸屈服强度 | ASTM D-638 | 290 | Kg/cm2 | ||
| 弯曲模量 | ASTM D-790 | 23000 | Kg/cm2 | ||
| 断裂伸长率 | ASTM D-638 | 40 | % | ||
| Izod缺口冲击强度 | ASTM D-256 | 60 | J/m | ||
| 拉伸屈服强度 | ASTM D-638 | 28 | MPa | ||
| Izod缺口冲击强度 | ASTM D-256 | 6 | Kg.cm/cm | ||
| 弯曲模量 | ASTM 790 | 2260 | MPa | ||
| 弯曲强度 | ASTM D-790 | 410 | Kg/cm2 | ||
| Izod缺口冲击强度 | ASTM D-256 | 1.1 | ft.lb/in | ||
| 弯曲强度 | ASTM D-790 | 40 | MPa | ||
| 弯曲强度 | ASTM D-790 | 5800 | psi | ||
| 热性能 | 热变形温度 | 0.45Mpa | ASTM D-648 | 137 | ℃ |
| 热变形温度 | 1.82Mpa | ASTM D-648 | 86 | ℃ | |
| 热变形温度 | 1.82Mpa | ASTM D-648 | 185 | °F | |
| 耐燃性 | ASTM UL94 | HB | class | ||
| 热变形温度 | 0.45Mpa | ASTM D-648 | 280 | °F | |