LDPE/756A/美国陶氏
- 生产企业： 美国陶氏
①原料描述部分
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | 薄膜级用 | ||
| 备注说明 | 产品商标DOW | ||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-792 | 0.925 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1338 | 6.4 | g/10min | |||
| 薄膜厚度 | 25.4 | μ | ||||
| 机械性能 | 屈服拉伸强度 | MD | ASTM D-882 | 13.9 | MPa | |
| TD | ASTM D-882 | 12.8 | MPa | |||
| 断裂拉伸强度 | MD | ASTM D-882 | 25.1 | MPa | ||
| TD | ASTM D-882 | 16.0 | MPa | |||
| 断裂伸长率 | MD | ASTM D-882 | 340 | % | ||
| TD | ASTM D-882 | 530 | % | |||
| 落镖冲击强度 | ASTM D-1709 | 36 | g | |||
| 埃尔曼多夫撕裂强度 | MD | ASTM D-1922 | 210 | g | ||
| TD | ASTM D-1922 | 180 | g | |||
| 热性能 | 维卡软化点 | ASTM D-1525 | 96.1 | ℃ | ||
| 熔点 | DSC | 113 | ℃ | |||
| 其它性能 | 薄膜韧性 | MD | ASTM D-882 | 141 | J/cm3 | |
| TD | ASTM D-882 | 132 | J/cm3 | |||
| 光学性能 | 光泽度 | 45° | ASTM D-2457 | 87 | ||
| 雾度 | ASTM D-1003 | 3.5 | % | |||