LDPE/611A/美国陶氏
- 生产企业： 美国陶氏
①原料描述部分
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | 薄膜级用 | ||
| 备注说明 | 产品商标DOW | ||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-792 | 0.924 | g/cm3 | ||
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.88 | g/10min | ||
| 薄膜厚度 | 50.8 | μ | ||||
| 切割模量 | MD | ASTM D-882 | 201 | MPa | ||
| TD | ASTM D-882 | 227 | MPa | |||
| 机械性能 | 薄膜强度 | MD | ASTM D-882 | 64.5 | J/cm3 | |
| TD | ASTM D-882 | 66.9 | J/cm3 | |||
| 屈服拉伸强度 | MD | ASTM D-882 | 11.8 | MPa | ||
| TD | ASTM D-882 | 12.2 | MPa | |||
| 断裂拉伸强度 | MD | ASTM D-882 | 21.6 | MPa | ||
| TD | ASTM D-882 | 16.9 | MPa | |||
| 断裂伸长率 | MD | ASTM D-882 | 370 | % | ||
| TD | ASTM D-882 | 560 | % | |||
| 落镖冲击强度 | ASTM D-1709 | 120 | g | |||
| 埃尔曼多夫撕裂强度 | MD | ASTM D-1922 | 400 | g | ||
| TD | ASTM D-1922 | 450 | g | |||
| 热性能 | 维卡软化点 | ASTM D-1525 | 97.2 | ℃ | ||
| 熔点 | DSC | 112 | ℃ | |||
| 光学性能 | 光泽度 | 45° | ASTM D-2457 | 76 | ||
| 雾度 | ASTM D-1003 | 7.0 | % | |||