LDPE/6330F/台湾塑胶
- 生产企业： 台湾塑胶
①原料描述部分
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | 用途：一般包装，积压膜。 | ||
| 备注说明 | 特性：光学性佳，刚性优良。 | ||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.924 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1238 | 2.1 | g/10min | |||
| 机械性能 | 拉力降伏强度 | ASTM D-638 | 100 | kg/cm2 | ||
| 拉力降伏强度 | MD | ASTM D-882B | 100 | kg/cm2 | ||
| TD | ASTM D-882B | 110 | kg/cm2 | |||
| 抗撕裂性 | MD | ASTM D-1922 | 70 | N/mm | ||
| TD | ASTM D-1922 | 50 | N/mm | |||
| 拉力断裂伸长率 | MD | ASTM D-882B | 280 | % | ||
| TD | ASTM D-882B | 580 | % | |||
| 弯曲模量 | ASTM D-790 | 1800 | kg/cm2 | |||
| 拉力断裂强度 | MD | ASTM D-882B | 230 | kg/cm2 | ||
| TD | ASTM D-882B | 180 | kg/cm2 | |||
| 1%伸长弹性系数 | MD | ASTM D-882B | 2000 | kg/cm2 | ||
| TD | ASTM D-882B | 2300 | kg/cm2 | |||
| 拉力断裂伸长率 | ASTM D-638 | 600 | % | |||
| 硬度 | ASTM D-2240 | 53 | Shore D | |||
| 拉力断裂强度 | ASTM D-638 | 150 | kg/cm2 | |||
| 摩擦系数 | ASTM D-1894 | >0.5 | ||||
| 落球行动强度 | ASTM D-1709 | 100 | g | |||
| 热性能 | 软化点 | ASTM D-1525 | 96 | ℃ | ||
| 脆化温度 | ASTM D-746 | <-70 | ℃ | |||
| 熔点 | DSC | 113 | ℃ | |||
| 其它性能 | 光泽度 | 45℃ | ASTM D-2457 | 95 | % | |
| 浊度 | ASTM D-1003 | 6.5 | % | |||
| 建设薄膜厚度 | ASTM D-1003 | 25～80 | µ | |||