LDPE/6320F/台湾塑胶
- 生产企业： 台湾塑胶
①原料描述部分
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | 一般薄膜 | ||
| 备注说明 | 具有良好的加工性和机械性 | ||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 2.2 | g/10min | ||
| 密度 | ASTM D-1505 | 0.921 | g/cm3 | |||
| 物理性能 | 薄膜厚度 | 30-80 | ||||
| 机械性能 | 断裂点伸长率 | MD | ASTM D-882B | 240 | % | |
| TD | ASTM D-882B | 600 | % | |||
| 落球冲击强度 | ASTM D-1709 | 115 | g | |||
| 降伏点强度 | MD | ASTM D-882B | 100 | kg/cm2 | ||
| TD | ASTM D-882B | 110 | kg/cm2 | |||
| 断裂点强度 | MD | ASTM D-882B | 250 | kg/cm2 | ||
| TD | ASTM D-882B | 190 | kg/cm2 | |||
| 热性能 | 软化点 | ASTM D-1525 | 93 | ℃ | ||
| 脆化温度 | ASTM D-746 | <-75 | ℃ | |||
| 熔点 | DSC | 111 | ℃ | |||
| 其它性能 | 抗撕裂性 | MD | ASTM D-1922 | 70 | N/mm | |
| TD | ASTM D-1922 | 45 | N/mm | |||
| 摩擦系数 | ASTM D-1894 | >0.5 | ||||
| 浊度 | ASTM D-1003 | 8 | % | |||
| 1%伸长弹性系数 | MD | ASTM D-882B | 1500 | kg/cm2 | ||
| TD | ASTM D-882B | 1700 | kg/cm2 | |||
| 光泽度 | 45℃ | ASTM D-2457 | 60 | % | ||