LLDPE/LL-1002/埃克森美孚
- 生产企业： 埃克森美孚
①原料描述部分
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | 包装袋、伸展薄膜、罐子、箱衬垫 | ||
| 备注说明 | |||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 2.0 | g/10min | ||
| 密度 | ExxonMobil Method | 0.918 | g/cm3 | |||
| 机械性能 | 极限伸长率 | MD | ASTM D-882 | 700 | % | |
| TD | ASTM D-882 | 830 | % | |||
| Elmendorf断裂强度 | MD | ASTM D-1922 | 150 | g | ||
| TD | ASTM D-1922 | 340 | g | |||
| 断裂拉伸强度 | MD | ASTM D-882 | 5800 | psi(MPa) | ||
| TD | ASTM D-882 | 4800 | psi(MPa) | |||
| 热性能 | 熔点 | ExxonMobil Method | 249(121) | ℉(℃) | ||
| 其它性能 | 击穿 | ExxonMobil Method | 20 | in.lb | ||
| 计量 | ASTM D-374 | 1.2 | mil | |||
| 1%割线模量 | MD | ASTM D-882 | 28 | psi(MPa) | ||
| TD | ASTM D-882 | 33 | psi(MPa) | |||
| 混浊度 | ASTM D-1003 | 18 | % | |||
| 屈服拉伸强度 | MD | ASTM D-882 | 1400 | psi(MPa) | ||
| TD | ASTM D-882 | 1400 | psi(MPa) | |||
| 光泽度 | ASTM D-2457 | 40 | ||||