LLDPE/1210/美国陶氏
- 生产企业： 美国陶氏
①原料描述部分
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | 工业，食品和特殊的包装 | ||
| 备注说明 | 良好热封性、加工性、含滑爽剂 | ||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-792 | 0.9190 | g/cc | ||
| 机械性能 | 屈服拉伸强度 | MD | ASTM D-882 | 10.3 | MPa | |
| TD | ASTM D-882 | 11.1 | MPa | |||
| 断裂拉伸强度 | MD | ASTM D-882 | 31.7 | MPa | ||
| TD | ASTM D-882 | 25.1 | MPa | |||
| 刺穿强度 | ASTM DOW | 8.2 | J/cm3 | |||
| Dart 冲击强度 | ASTM D-1709 | <100 | g | |||
| 热性能 | 维卡软化点 | ASTM D-1525 | 101 | ℃ | ||
| 其它性能 | 断裂伸长率 | MD | ASTM D-882 | 658 | % | |
| TD | ASTM D-882 | 714 | % | |||
| 熔融指数 | ASTM D-1238 | 1.00 | g/10min | |||
| 熔点 | ASTM DOW | 108 | ℃ | |||
| 抗撕裂性 | MD | ASTM D-1992 | 106 | g | ||
| TD | ASTM D-1992 | 256 | g | |||
| 光泽度 | 20° | ASTM D-2457 | 69 | |||
| 拉伸模量 | MD | ASTM D-882 | 183.3 | MPa | ||
| TD | ASTM D-882 | 217.4 | MPa | |||
| 韧性 | MD | ASTM D-882 | 102.6 | J/cm3 | ||
| TD | ASTM D-882 | 98.1 | J/cm3 | |||
| TD | ASTM D-882 | 98.1 | J/cm3 | |||
| 透明度 | ASTM D-1746 | 95 | ||||
| 雾度 | ASTM D-1003 | 10.8 | % | |||