LLDPE/HS-7094 NT 7/美国陶氏
- 生产企业： 美国陶氏
①原料描述部分
| 规格级别 | 其它 其它 吹塑 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | |||
| 备注说明 | |||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||
| 基本性能 | 比重 | ASTM D-792 | 0.93 | g/cm3 | ||||
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.8 | g/10min | ||||
| 机械性能 | 电影穿刺能源 | 20.3um | Internal Method | 1.47 | J | |||
| 电影穿刺能源 | 50.8um | Internal Method | 3.16 | J | ||||
| 电影穿刺力 | 20.3um | Internal Method | 31.1 | N | ||||
| 电影穿刺力 | 50.8um | Internal Method | 66.7 | N | ||||
| 电影穿刺抵抗 | 20.3um | Internal Method | 8.36 | J/cm3 | ||||
| 电影穿刺抵抗 | 50.8um | Internal Method | 7.03 | J/cm3 | ||||
| 电影韧性 | 20.3um | ASTM D-882 |
| J/cm3 | ||||
| 电影韧性 | 50.8um | ASTM D-882 |
| J/cm3 | ||||
| 割线模量-2% Secant | 20.3um | ASTM D-882 |
| MPa | ||||
| 割线模量-2% Secant | 50.8um | ASTM D-882 |
| MPa | ||||
| 拉伸屈服强度 | 20.3um | ASTM D-882 |
| MPa | ||||
| 拉伸屈服强度 | 50.8um | ASTM D-882 |
| MPa | ||||
| 拉伸断裂强度 | 20.3um | ASTM D-882 |
| MPa | ||||
| 拉伸断裂强度 | 50.8um | ASTM D-882 |
| MPa | ||||
| 拉伸断裂伸长率 | 20.3um | ASTM D-882 |
| % | ||||
| 拉伸断裂伸长率 | 50.8um | ASTM D-882 |
| % | ||||
| 落锤冲击 | 20.3um | ASTM D-1709A | 52 | g | ||||
| 落锤冲击 | 20.3um | ASTM D-1709B | <100 | g | ||||
| 落锤冲击 | 50.8um | ASTM D-1709A | 170 | g | ||||
| 落锤冲击 | 50.8um | ASTM D-1709B | <100 | g | ||||
| 埃尔曼多夫撕裂强度 | 20.3um | ASTM D-1922 |
| g | ||||
| 埃尔曼多夫撕裂强度 | 50.8um | ASTM D-1922 |
| g | ||||
| 密封起始温度 | 20.3um | Internal Method | 120 | ℃ | ||||
| 密封起始温度 | 50.8um | Internal Method | 130 | ℃ | ||||
| 密封强度 | 160℃，0.0203mm | Internal Method | 1500 | g | ||||
| 密封强度 | 170℃，0.0508mm | Internal Method | 2600 | g | ||||
| 加工性能 | 熔体温度 | 233 | ℃ | |||||
| 热性能 | 维卡软化点 | ASTM D-1525 | 114 | ℃ | ||||
| 熔化温度 | Internal Method | 126 | ℃ | |||||
| 光学性能 | 光泽度 | 20°，20.3um | ASTM D-2457 | 23 | ||||
| 光泽度 | 20°，50.8um | ASTM D-2457 | 26 | |||||
| 光泽度 | 45°，20.3um | ASTM D-2457 | 43 | |||||
| 光泽度 | 45°，50.8um | ASTM D-2457 | 44 | |||||
| 雾度 | 20.3um | ASTM D-1003 | 18 | % | ||||
| 雾度 | 50.8um | ASTM D-1003 | 21 | % | ||||