LLDPE/FN410/韩国SK
- 生产企业： 韩国SK
①原料描述部分
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | 制造不具滑性的一般薄膜而研制 | ||
| 备注说明 | 具有优秀的引张强度、引裂强度、无胶凝、耐阻塞性和密封强度 | ||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.919 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1238 | 1 | g/10min | |||
| 机械性能 | 抗冲击强度 | ASTM D-3420 | 10 | Kg/cm | ||
| 拉伸断裂强度 | MD | ASTM D-882 | 430 | Kg/cm2 | ||
| TD | ASTM D-882 | 360 | Kg/cm2 | |||
| 拉伸屈服强度 | MD | ASTM D-882 | 120 | Kg/cm2 | ||
| TD | ASTM D-882 | 110 | Kg/cm2 | |||
| 伸长率 | MD | ASTM D-882 | 750 | % | ||
| TD | ASTM D-882 | 850 | % | |||
| 撕裂弹性率 | MD | ASTM D-882 | 2，000 | Kg/cm2 | ||
| TD | ASTM D-882 | 2，500 | Kg/cm2 | |||
| 撕裂强度 | MD | ASTM D-1004 | 5 | Kg/cm | ||
| TD | ASTM D-1004 | 12 | Kg/cm | |||
| 伸长率 | MD | ASTM D-882 | 750 | % | ||
| TD | ASTM D-882 | 850 | % | |||
| 热性能 | 脆化温度 | ASTM D-746 | <-70 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 102 | ℃ | |||
| 其它性能 | 薄膜厚度 | ASTM D-746 | 50 | µm | ||
| 雾度 | ASTM D-1003 | 20 | % | |||