LLDPE/3410/台湾塑胶
- 生产企业： 台湾塑胶
①原料描述部分
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | 超薄膜，点断袋，高滑动性薄膜，掺於收缩膜改，善薄膜烧断。 | ||
| 备注说明 | 特性：热封性佳，薄膜延伸性佳，刚性适中，高韧性，3414开口佳。 | ||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.926 | g/cm3 | ||
| 熔体流动速率 | ASTM D-1238 | 1.0 | g/10min | |||
| 机械性能 | 拉力降伏强度 | MD | ASTM D-882B | 120 | kg/cm2 | |
| TD | ASTM D-882B | 130 | kg/cm2 | |||
| 落球冲击强度 | ASTM D-1709 | 90 | g | |||
| 拉力断裂强度 | MD | ASTM D-882B | 440 | kg/cm2 | ||
| TD | ASTM D-882B | 340 | kg/cm2 | |||
| 抗撕裂性 | MD | ASTM D-1922 | 80 | g/25µm | ||
| TD | ASTM D-1922 | 350 | g/25µm | |||
| 1%伸长弹性系数 | MD | ASTM D-882B | 2300 | kg/cm2 | ||
| TD | ASTM D-882B | 3100 | kg/cm2 | |||
| 拉力断裂伸长率 | MD | ASTM D-882B | 600 | % | ||
| TD | ASTM D-882B | 800 | % | |||
| 热性能 | 脆化温度 | ASTM D-746 | <-70 | ℃ | ||
| 软化点 | ASTM D-1525 | 95 | ℃ | |||
| 熔点 | DSC | 124 | ℃ | |||
| 其它性能 | 透明度 | 55 | % | |||
| 开口剂 | 无 | |||||
| 滑剂 | 无 | |||||
| 浊度 | ASTM D-1003 | 15 | % | |||
| 光泽度 | 45℃ | ASTM D-2457 | 44 | % | ||