LLDPE/FT610U/韩国SK
- 生产企业： 韩国SK
①原料描述部分
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | T-模，工业用 | ||
| 备注说明 | 特性：抗张强度、加工性、透明性 | ||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 2.1 | g/10min | ||
| 密度 | ASTM D-1505 | 0.918 | g/10min | |||
| 物理性能 | 薄膜厚度 | 25 | μm | |||
| 机械性能 | 断裂拉伸强度 | MD | ASTM D-882 | 380 | Kg/cm2 | |
| TD | ASTM D-882 | 330 | Kg/cm2 | |||
| 屈服拉伸强度 | MD | ASTM D-882 | 140 | Kg/cm2 | ||
| TD | ASTM D-882 | 130 | Kg/cm2 | |||
| 尖头冲击强度 | ASTM D-1709 | 3.5 | g/μm | |||
| 断裂伸长率 | MD | ASTM D-882 | 650 | % | ||
| TD | ASTM D-882 | 800 | % | |||
| 抗张模数 | MD | ASTM D-882 | 2200 | Kg/cm2 | ||
| TD | ASTM D-882 | 3100 | Kg/cm2 | |||
| 撕裂强度 | MD | ASTM D-1004 | 115 | kg/cm | ||
| TD | ASTM D-1004 | 105 | kg/cm | |||
| 热性能 | 低温脆化温度 | ASTM D-746 | <-75 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 98 | ℃ | |||