PC/ABS/GP-5206F/LG化学
- 生产企业： LG化学
①原料描述部分
| 规格级别 | 增强 其它 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | |||
| 备注说明 | 高强度 | ||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D792 | 1.35 | |||
| 成型收缩率 | ASTM D955 | 0.2-0.4 | % | |||
| 机械性能 | 拉伸强度 | - | ASTM D638 | 950 | kg/cm2 | |
| - | ASTM D638 | 93 | MPa | |||
| - | ASTM D638 | 13500 | psi | |||
| 断裂伸长率 | ASTM D638 | 4 | % | |||
| 弯曲强度 | - | ASTM D790 | 1400 | kg/cm2 | ||
| - | ASTM D790 | 137 | MPa | |||
| - | ASTM D790 | 19900 | psi | |||
| 弯曲模量 | - | ASTM D790 | 58000 | kg/cm2 | ||
| - | ASTM D790 | 5685 | MPa | |||
| - | ASTM D790 | 825 | psi | |||
| Izod缺口冲击强度 | - | 23℃ | ASTM D256 | 7 | Kg.cm/cm | |
| - | 23℃ | ASTM D256 | 69 | J/m | ||
| - | 23℃ | ASTM D256 | 1.3 | ft.ib/in | ||
| 洛氏硬度 | ASTM D785 | 117 | R | |||
| 热性能 | 热变形温度 | - | 1.82MPa | ASTM D648 | 120 | ℃ |
| - | 1.82MPa | ASTM D648 | 250 | ℉ | ||
| 阻燃性 | 1.7mm | UL94 | V-0 | |||