PPS/JB-B7-4/聚赛龙
- 生产企业： 聚赛龙
①原料描述部分
| 规格级别 | 增强 其它 其它 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | |||
| 备注说明 | |||
②加工条件
| 加工条件 |
|---|
③原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 比重 | ASTM D-792 | 1.88 | g/cm3 | ||
| 成型收缩率 | TD | ASTM D-955 | 0.3 | % | ||
| MD | ASTM D-955 | 0.2 | % | |||
| 机械性能 | 拉伸强度 | ASTM D-638 | 75 | Mpa | ||
| 断裂伸长率 | ASTM D-638 | 1.3 | % | |||
| 弯曲弹性模量 | ASTM D-790 | 16 | ||||
| IZOD冲击强度(缺口) | ASTM D-256 | 5.5 | KJ/m2 | |||
| 弯曲强度 | ASTM D-790 | 160 | Mpa | |||
| 电气性能 | 介质损耗角正切 | ASTM D-150 | 0.0015 | 1MHz | ||
| 介电强度 | ASTM D-149 | 16 | Kv/mm | |||
| 体积电阻率 | ASTM D-257 | 1016 | Ω﹒cm | |||
| 介电常数 | ASTM D-150 | 4.9 | 1KHz | |||
| 热性能 | 线形热膨胀系数 | TD | ASTM D-696 | 2.3 | ||
| MD | ASTM D-696 | 1.5 | ||||
| 阻燃性 | UL-94 | V-0 | ||||
| 热变形温度 | 1.80MPa | ASTM D-648 | 260 | ℃ | ||
| 其它性能 | 吸水率 | (23℃.24h) | ASTM D-570 | 0.02 | ||