PA12/3035U/日本宇部
- 生产企业: 日本宇部
①原料描述部分
规格级别 | 其它 其它 其它 | 外观颜色 | |
---|---|---|---|
该料用途 | |||
备注说明 | 特性:高粘度 |
②加工条件
加工条件 |
---|
③原料技术数据
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 成型收缩率 | UBEmethod | 1.0 | % | |
成型收缩率 | UBEmethod | 1.6 | % | ||
吸水率 | ASTM D-570 | 1.5 | % | ||
吸水率 | ASTM D-570 | 0.25 | % | ||
物理性能 | 比重 | ASTM D-792 | 1.02 | ||
机械性能 | 弯曲弹性率 | -30° | ASTM D-790 | 17000 | kgf/cm2 |
挤剪强度 | 23° | ASTM D-732 | 350 | kgf/cm2 | |
抗冲击强度 | 23° | ASTM D-256 | 22 | kgf.cm/cm | |
弯曲强度 | 23° | ASTM D-790 | 560 | kgf/cm2 | |
屈服下的伸张强度 | 23° | ASTM D-638 | 430 | kgf/cm2 | |
弯曲弹性率 | 80° | ASTM D-790 | 3400 | kgf/cm2 | |
TABER磨耗率 | ASTM D-1044 | 5 | mg | ||
弯曲强度 | -30° | ASTM D-790 | 880 | kgf/cm2 | |
屈服下的伸张强度 | -30° | ASTM D-638 | 770 | kgf/cm2 | |
弯曲强度 | 80° | ASTM D-790 | 170 | kgf/cm2 | |
断裂下的延伸率 | 23° | ASTM D-638 | >250 | % | |
屈服下的延伸率 | 23° | ASTM D-638 | 19 | % | |
弯曲弹性率 | 23° | ASTM D-790 | 14500 | kgf/cm2 | |
抗冲击强度 | -30° | ASTM D-256 | 8.0 | kgf.cm/cm | |
屈服下的延伸率 | 23° | ASTM D-638 | 12 | % | |
断裂下的伸张强度 | 23° | ASTM D-638 | >550 | kgf/cm2 | |
1%变形下的压缩强度 | 23° | ASTM D-695 | 130 | kgf/cm2 | |
弯曲强度 | 23° | ASTM D-790 | 380 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 105 | ||
抗冲击强度 | 23° | ASTM D-256 | 13 | kgf.cm/cm | |
屈服下的伸张强度 | 80° | ASTM D-638 | 190 | kgf/cm2 | |
断裂下的伸张强度 | 23° | ASTM D-638 | >500 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 110 | ||
弯曲弹性率 | 23° | ASTM D-790 | 10000 | kgf/cm2 | |
屈服下的伸张强度 | 23° | ASTM D-638 | 380 | kgf/cm2 | |
电气性能 | 介电损耗 | 60HZ | ASTM D-150 | 0.03 | |
抗电弧强度 | ASTM D-495 | 180 | S | ||
介电常数 | 106HZ | ASTM D-150 | 2.9 | ||
绝缘耐力 | ASTM D-149 | 30 | KV/mm | ||
介电常数 | 60HZ | ASTM D-150 | 3.4 | ||
体积电阻率 | ASTM D-257 | 1015 | Ω.cm | ||
体积电阻率 | ASTM D-257 | 1014 | Ω.cm | ||
IEC电路 | UL746 | 600+ | V | ||
介电损耗 | 106HZ | ASTM D-150 | 0.02 | ||
介电损耗 | 103HZ | ASTM D-150 | 0.03 | ||
介电常数 | 103HZ | ASTM D-150 | 3.3 | ||
热性能 | 熔点 | ASTM DSC | 176-180 | °C | |
线性热膨胀系数 | ASTM D-696 | 10 | X的10-5cm/cm/°C | ||
热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 145 | °C |