Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.15
|
g/cm³
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)
|
87.0
|
cm³/10min
|
ISO 1133 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
3420
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break)
|
66.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
2.3
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
3190
|
MPa
|
ISO 178 |
|
Flexural Strength
|
123
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
2.0
|
kJ/m²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength
|
15
|
kJ/m²
|
ISO 179/1eU |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
97.0
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
244
|
°C
|
ISO 306/B50 |
|
Melting Temperature
|
262
|
°C
|
ISO 11357-3 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
< 80.0
|
°C
|
|
|
Drying Time
|
2.0 to 12
|
hr
|
|
|
Processing (Melt) Temp
|
280 to 300
|
°C
|
|
|
Mold Temperature
|
80.0 to 120
|
°C
|