| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.18
|
g/cm³
|
ISO 1183 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
3400
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break)
|
85.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
4.0
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
3300
|
MPa
|
ISO 178 |
|
Flexural Strength
|
120
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
2.0
|
kJ/m²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength (23°C)
|
26
|
kJ/m²
|
ISO 179/1eU |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
85.0
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
200
|
°C
|
ISO 306/B50 |
|
Melting Temperature
|
250 to 255
|
°C
|
DSC |
| Injection |
Nominal Value
|
Unit
|
|
|
Processing (Melt) Temp
|
260 to 290
|
°C
|
|
|
Mold Temperature
|
80.0 to 120
|
°C
|