| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
2.54
|
g/cm³
|
ISO 1183 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Ball Indentation Hardness (H 961/30)
|
219
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
7000
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break)
|
40.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
1.5
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
10000
|
MPa
|
ISO 178 |
|
Flexural Strength
|
50.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
3.0
|
kJ/m²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength (23°C)
|
8.0
|
kJ/m²
|
ISO 179/1eU |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
131
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
> 200
|
°C
|
ISO 306/B50 |
|
Thermal Conductivity
|
2.0
|
W/m/K
|
ISO 22007-2.2 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
> 1.0E+12
|
ohm
|
IEC 60093 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating (3.20 mm)
|
HB
|
|
UL 94 |
|
Glow Wire Flammability Index (1.00 mm)
|
650
|
°C
|
IEC 60695-2-12 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80.0
|
°C
|
|
|
Drying Time
|
2.0 to 20
|
hr
|
|
|
Processing (Melt) Temp
|
300 to 320
|
°C
|
|
|
Mold Temperature
|
> 100
|
°C
|