Anjacom® PC/ABS 050/65S-UV|(PC+ABS)|almaak物性表报告及物性特性介绍,Anjacom® PC/ABS 050/65S-UV|(PC+ABS)|almaak注塑参数详情-塑料物性表查询网

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
熔体体积流动速率(Melt volume-flow rate) (MVR)	22	cm³/10min	ISO 1133
温度(Temperature)	260	°C	ISO 1133
负载(Load)	5	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	0.6	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	0.6	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	2300	MPa	ISO 527-1/-2
屈服应力(Yield stress)	56	MPa	ISO 527-1/-2
屈服应变(Yield strain)	5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	49	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	105	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	127	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	122	°C	ISO 306
Burning behav. at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6	mm	IEC 60695-11-10

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
电气强度(Electric strength)	24	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	300	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
吸水率(Water absorption)	0.7	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.2	%	Sim. to ISO 62
密度(Density)	1130	kg/m³	ISO 1183

CharacteristicsDelivery formNatural ColorSpecial CharacteristicsU.V. stabilized or stable to weatherRegional AvailabilityEuropeDisclaimerCopyright M-Base Engineering+Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.