Bayblend® ET3032 FR|(PC+ABS)-I-MD10 FR(40+72)|Bayer MatSc物性表报告及物性特性介绍,Bayblend® ET3032 FR|(PC+ABS)-I-MD10 FR(40+72)|Bayer MatSc注塑参数详情-塑料物性表查询网

Product TextsRubber modified PC blend10 % mineral filledflame-retardantextrusion gradeVicat/B 120 temperature = 108 °Cgood extrusion and vacuum-forming behaviourUL 94 V-0 (0.75 mm) (Bayer internal test)halogen-free according to DIN VDE 0472-815 glow wire temperature (GWFI): 960 °C at 2.0 mm.

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	10	cm³/10min	ISO 1133
温度(Temperature)	260	°C	ISO 1133
负载(Load)	5	kg	ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	3950	MPa	ISO 527-1/-2
屈服应力(Yield stress)	63	MPa	ISO 527-1/-2
屈服应变(Yield strain)	4	%	ISO 527-1/-2

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
维卡软化温度（50℃/ h的50N）Vicat softening temperature	106	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	48	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	59	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at thickness h	V-0	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). 5V at thickness h	5VB	class	IEC 60695-11-20
厚度测试(Thickness tested)	2.0	mm	IEC 60695-11-20

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.5	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.2	%	Sim. to ISO 62
密度(Density)	1300	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	260	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	240	mm/s	ISO 294

Diagrams M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.