Delrin® 100PE NC010|POM|DuPont物性表报告及物性特性介绍,Delrin® 100PE NC010|POM|DuPont注塑参数详情-塑料物性表查询网

Product TextsCommon features of Delrin® acetal resin include mechanical and physical properties such as high mechanical strength and rigidity, excellent fatigue and impact resistance, as well as resistance to moisture, gasoline, lubricants, solvents and many other neutral chemicals. Delrin® acetal resins also have excellent dimensional stability and good electrical insulating characteristics. They are naturally resilient, self-lubricating and available in a variety of colours and speciality grades. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-17 kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed. It has the best combination of strength and toughness and improved processing productivity for injection molding. 9	cm³/10min	ISO 1133
温度(Temperature)	190	°C	ISO 1133
负载(Load)	2.16	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	2.1	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.9	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	2900	MPa	ISO 527-1/-2
屈服应力(Yield stress)	70	MPa	ISO 527-1/-2
屈服应变(Yield strain)	22	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	50	%	ISO 527-1/-2
Tensile creep modulus (1h)	2700	MPa	ISO 899-1
Tensile creep modulus (1000h)	1500	MPa	ISO 899-1
简支梁冲击强度(Charpy impact strength) (+23°C)	N	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	350	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	14	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	10	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	178	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	100	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	160	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	160	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	110	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	110	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8	mm	IEC 60695-11-10
Oxygen index	17	%	ISO 4589-1/-2

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	3.8	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	3.7	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	200	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	40	E-4	IEC 60250
体积电阻率(Volume resistivity)	1E12	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
电气强度(Electric strength)	32	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	600	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1420	kg/m³	ISO 1183

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density) of melt	1170	kg/m³	-
熔体热导率(Thermal conductivity of melt)	0.22	W/(m K)	-
规格的热容融化(Spec. heat capacity of melt)	3000	J/(kg K)	-

Diagrams M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.