HOSTAFORM MT8R02|POM|Ticona物性表报告及物性特性介绍,HOSTAFORM MT8R02|POM|Ticona注塑参数详情-塑料物性表查询网

Product TextsHostaform® acetal copolymer grade MT8R02 is a special grade developed

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	8.5	cm³/10min	ISO 1133
温度(Temperature)	190	°C	ISO 1133
负载(Load)	2.16	kg	ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	2700	MPa	ISO 527-1/-2
屈服应力(Yield stress)	62	MPa	ISO 527-1/-2
屈服应变(Yield strain)	9	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	30	%	ISO 527-1/-2
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	8	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	166	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	82	°C	ISO 75-1/-2

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1400	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Processing conditions acc. ISO	9990	-	ISO ....-2
Injection Molding, melt temperature	205	°C	ISO 294
Injection Molding, mold temperature	90	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294
Injection Molding, pressure at hold	90	MPa	ISO 294

CharacteristicsProcessingInjection MoldingDelivery formPelletsAdditivesLubricants, Release agentRegional AvailabilityNorth America, Europe, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSING 40 mm Water content 0,2%g. moisturizing is not necessary.

Application examples
Injection system

DisclaimerCopyright M-Base Engineering+Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.