HOSTAFORM S 9362|POM|Ticona 物性表: HOSTAFORM S 9362|POM|Ticona物性表及特性介绍,HOSTAFORM S 9362|POM|Ticona注塑参数详情,如需HOSTAFORM S 9362|POM|Ticona下载, 可到相关下载区下载
Product TextsPreliminary Data SheetHostaform® S 9362 provides 5
cm³/10min
ISO 1133
温度(Temperature)
190
°C
ISO 1133
负载(Load)
2.16
kg
ISO 1133
成型收缩(Molding shrinkage) (parallel)
1.9
%
ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)
1.8
%
ISO 294-4, 2577
机械性能(机械性能(Mechanical properties))
值(Value)
单位(Unit)
测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)
2300
MPa
ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (-30°C)
190
kJ/m²
ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)
10
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)
6
kJ/m²
ISO 179/1eA
热性能(热性能(Thermal properties))
值(Value)
单位(Unit)
测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)
166
°C
ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)
87
°C
ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)
151
°C
ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature
144
°C
ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)
110
E-6/K
ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)
110
E-6/K
ISO 11359-1/-2
其他属性(Other properties)
值(Value)
单位(Unit)
测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)
0.8
%
Sim. to ISO 62
吸湿性(Humidity absorption)
0.25
%
Sim. to ISO 62
密度(Density)
1390
kg/m³
ISO 1183
Test specimen production
值(Value)
单位(Unit)
测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Processing conditions acc. ISO
9990
-
ISO ....-2
Injection Molding, melt temperature
205
°C
ISO 294
Injection Molding, mold temperature
80
°C
ISO 10724
Injection Molding, injection velocity
200
mm/s
ISO 294
Injection Molding, pressure at hold
86
MPa
ISO 294
CharacteristicsProcessingInjection Molding, Profile ExtrusionDelivery formPelletsAdditivesRelease agentRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSING 40 mm Water content 0,2%g. moisturizing is not necessary.DisclaimerCopyright M-Base Engineering+Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.