Lexan JK500|(PC+ABS)-GX10|SABIC_IP物性表报告及物性特性介绍,Lexan JK500|(PC+ABS)-GX10|SABIC

加工/物理特性	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
熔体流动指数(Melt Flow Index)	20	g/10min	ASTM D 1238
温度(Temperature)	260	°C	-
负载(Load)	2.16	kg	-
模具收缩(Mold Shrinkage) (MD)	0.00175	mm/mm	ASTM D 955
密度(Density) (73°F)	1270	kg/m³	ASTM D 792

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	5250	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	70	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	2.1	%	ISO 527-1/-2
弯曲弹性模量(Flexural modulus) (23°C)	4590	MPa	ISO 178
悬臂梁式冲击切口 (23°C)	5	kJ/m²	ISO 180/1A
悬臂梁式冲击无切口(Izod Impact unnotched) (23°C)	21	kJ/m²	ISO 180/1U
ASTM数据(ASTM Data)
拉伸模量(Tensile Modulus)	4820	MPa	ASTM D 638
抗拉强度(Tensile Strength) at Yield	68	MPa	ASTM D 638
抗拉强度(Tensile Strength) at Break	68	MPa	ASTM D 638
屈服伸长率(Elongation at Yield)	5	%	ASTM D 638
断裂伸长率(Elongation at Break)	5	%	ASTM D 638
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	4340	MPa	ASTM D 790
悬臂梁式冲击切口 (1/8 in)	0.0557	kJ/m	ASTM D 256

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	43	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	83	E-6/K	ISO 11359-1/-2
ASTM数据(ASTM Data)
UL 94 阻燃等级(Flame rating)	V-0	-	UL 94
厚度测试(Thickness tested)	0.99	mm	-
热膨胀系数(Coefficient of Thermal Expansion) (MD)	43.2	E-6/K	ASTM D 696
热膨胀系数(Coefficient of Thermal Expansion) (TD)	72	E-6/K	ASTM D 696
DTUL @ 66 psi	96	°C	ASTM D 648
DTUL @ 264 psi	88	°C	ASTM D 648
Vicat 温度(Temperature)	110	°C	ASTM D 1525

CharacteristicsProcessingInjection MoldingSpecial CharacteristicsFlame retardantRegional AvailabilityAsia PacificDisclaimerCopyright M-Base Engineering+Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.