POLYblend 83FR|(PC+ABS)|Polykemi物性表报告及物性特性介绍,POLYblend 83FR|(PC+ABS)|Polykemi注塑参数详情-塑料物性表查询网

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
成型收缩(Molding shrinkage) (parallel)	0.6	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	0.6	%	ISO 294-4, 2577
熔体流动指数(熔体流动指数(Melt flow index)) (MFI)	35	g/10min	ISO 1133
MFI温度(MFI temperature)	260	°C	ISO 1133
MFI负载(MFI load)	5	kg	ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
抗拉强度(Tensile Strength)	70	MPa	ISO 527-1/-2
屈服应变(Yield strain)	8	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	15	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	7	kJ/m²	ISO 179/1eA
弯曲弹性模量(Flexural modulus) (23°C)	2600	MPa	ISO 178

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	82	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	92	°C	ISO 75-1/-2
Vicat softening temperature A	105	°C	ISO 306
维卡软化温度（50℃/ h的50N）Vicat softening temperature	97	°C	ISO 306
Burning behav. at 1.5 mm nom. thickn.	V-0	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6	mm	IEC 60695-11-10
UL 识别(recognition)	UL	-	-

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
密度(Density)	1200	kg/m³	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formGranulesSpecial CharacteristicsFlame retardantRegional AvailabilityEurope, Asia PacificDisclaimerCopyright M-Base Engineering+Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.