Badamid® LA70 GF50 HH|PA66-GF50|Bada物性表报告及物性特性介绍,Badamid® LA70 GF50 HH|PA66-GF50|Bada注塑参数详情-塑料物性表查询网

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	16500 / 12500	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	230 / 180	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	2.5 / 3.5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	95 / 100	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	85 / -	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	17 / 21	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	13 / -	kJ/m²	ISO 179/1eA
悬臂梁式冲击切口 (23°C)	13 / 14.5	kJ/m²	ISO 180/1A

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据
熔化温度(熔化温度(Melting temperature)) (10°C/min)	260 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	250 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	250 / *	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	12.5 / *	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	55 / *	E-6/K	ISO 11359-1/-2
Burning behav. at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据
相对介电常数(Relative permittivity) (1MHz)	3.8 / 6.6	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	150 / 1700	E-4	IEC 60250
体积电阻率(Volume resistivity)	1E11 / 1E8	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	* / 1E10	Ohm	IEC 60093
相比漏电起痕指数(Comparative tracking index)	550 / -	-	IEC 60112

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据
吸水率(Water absorption)	4 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	1.2 / *	%	Sim. to ISO 62
密度(Density)	1550 / -	kg/m³	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formGranulesSpecial CharacteristicsHeat stabilized or stable to heatFeaturesThermal StabilityRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaDisclaimerCopyright M-Base .