SCHULAMID® 66 GBF 3020|PA66-(GB+GF)30|A. Schulman物性表报告及物性特性介绍,SCHULAMID® 66 GBF 3020|PA66-(GB+GF)30|A. Schulman注塑参数详情-塑料物性表查询网

Schulman Product Texts30% glass fibre and glass bead reinforced PA 66 with high mechanical strength and dimensional stability5 / 4.5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	40 / 50	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	35 / 45	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	8 / 13	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	6 / 10	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	263 / *	°C	ISO 11357-1/-3
玻璃化转变温度(Glass transition temperature) (10°C/min)	50 / *	°C	ISO 11357-1/-2
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	245 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	245 / *	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	235 / *	°C	ISO 306
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
ASTM数据(ASTM Data)
UL 94 阻燃等级(Flame rating)	HB	-	UL 94
厚度测试(Thickness tested)	3.2	mm	-

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
体积电阻率(Volume resistivity)	>1E13 / 1E10	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	* / >1E15	Ohm	IEC 60093
相比漏电起痕指数(Comparative tracking index)	- / 450	-	IEC 60112

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸湿性(Humidity absorption)	1.5 / *	%	Sim. to ISO 62
密度(Density)	1350 / -	kg/m³	ISO 1183

材料特殊性能(Material specific properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
粘数(Viscosity number)	145 / *	cm³/g	ISO 307, 1157, 1628

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density) of melt	1210	kg/m³	-
熔体热导率(Thermal conductivity of melt)	0.35	W/(m K)	-
规格的热容融化(Spec. heat capacity of melt)	1500	J/(kg K)	-
Eff. thermal diffusivity	7.50E-8	m²/s	-
喷射温度(Ejection temperature)	160	°C	-

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Processing conditions acc. ISO	1870	-	ISO ....-2
Injection Molding, melt temperature	290	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	250	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

CharacteristicsProcessingInjection MoldingDelivery formGranulesAdditivesRelease agentRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSINGPretreatment .