Schulman Product Texts25% mineral and 15% glass fibre reinforced PA 66 compound005	mm/mm	ASTM D 955
密度(Density) (73°F)	1470	kg/m³	ASTM D 792

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	8300 / 5000	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	120 / 80	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	2.5 / 6.5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	40 / 58	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	36 / -	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	4 / 5	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	3 / -	kJ/m²	ISO 179/1eA
ASTM数据(ASTM Data)
抗拉强度(Tensile Strength) at Break	130	MPa	ASTM D 638
断裂伸长率(Elongation at Break)	3	%	ASTM D 638
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	8991.44	MPa	ASTM D 790
抗弯强度(Flexural Strength)	170	MPa	ASTM D 790
悬臂梁式冲击切口 (1/8 in)	0.0534	kJ/m	ASTM D 256

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	263 / *	°C	ISO 11357-1/-3
玻璃化转变温度(Glass transition temperature) (10°C/min)	50 / *	°C	ISO 11357-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	236 / *	°C	ISO 306
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.2 / *	mm	IEC 60695-11-10
ASTM数据(ASTM Data)
DTUL @ 66 psi	254	°C	ASTM D 648
DTUL @ 264 psi	225	°C	ASTM D 648

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
体积电阻率(Volume resistivity)	>1E13 / 1E10	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	* / >1E15	Ohm	IEC 60093

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸湿性(Humidity absorption)	1.6 / *	%	Sim. to ISO 62
密度(Density)	1440 / -	kg/m³	ISO 1183

材料特殊性能(Material specific properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
粘数(Viscosity number)	140 / *	cm³/g	ISO 307, 1157, 1628

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density) of melt	1320	kg/m³	-
熔体热导率(Thermal conductivity of melt)	0.34	W/(m K)	-
规格的热容融化(Spec. heat capacity of melt)	1600	J/(kg K)	-
Eff. thermal diffusivity	7.50E-8	m²/s	-
喷射温度(Ejection temperature)	160	°C	-

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Processing conditions acc. ISO	1870	-	ISO ....-2
Injection Molding, melt temperature	290	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	250	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

CharacteristicsProcessingInjection MoldingDelivery formGranulesAdditivesRelease agentRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSINGPretreatment .