Stat-kon 9X04323|(PPA+PA66)-CD|SABIC_IP物性表报告及物性特性介绍,Stat-kon 9X04323|(PPA+PA66)-CD|SABIC

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	2780	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	58	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3.5	%	ISO 527-1/-2
弯曲弹性模量(Flexural modulus) (23°C)	2590	MPa	ISO 178
悬臂梁式冲击切口 (23°C)	3	kJ/m²	ISO 180/1A
ASTM数据(ASTM Data)
拉伸模量(Tensile Modulus)	2760	MPa	ASTM D 638
抗拉强度(Tensile Strength) at Yield	59	MPa	ASTM D 638
抗拉强度(Tensile Strength) at Break	56	MPa	ASTM D 638
屈服伸长率(Elongation at Yield)	3.7	%	ASTM D 638
断裂伸长率(Elongation at Break)	3.7	%	ASTM D 638
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	2400	MPa	ASTM D 790
抗弯强度(Flexural Strength)	99	MPa	ASTM D 790
悬臂梁式冲击切口 (1/8 in)	0.032	kJ/m	ASTM D 256

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	163	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	181	°C	ISO 75-1/-2
ASTM数据(ASTM Data)
热膨胀系数(Coefficient of Thermal Expansion) (MD)	22	E-6/K	ASTM D 696
热膨胀系数(Coefficient of Thermal Expansion) (TD)	24	E-6/K	ASTM D 696
DTUL @ 66 psi	180	°C	ASTM D 648
DTUL @ 264 psi	168	°C	ASTM D 648

CharacteristicsProcessingInjection MoldingSpecial CharacteristicsIncreased electrical conductivityRegional Availability .