Ultramid® A3L HP|PA66|BASF物性表报告及物性特性介绍,Ultramid® A3L HP|PA66|BASF注塑参数详情-塑料物性表查询网

Product TextsUltramid A3L HP is an unreinforced, impact modified, high flow, Polyamid 66 for injection molding. This grade has excellent flow and improved ambient and low temperature toughness.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	2440 / -	MPa	ISO 527-1/-2
屈服应力(Yield stress)	63.5 / -	MPa	ISO 527-1/-2
屈服应变(Yield strain)	6.2 / -	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	28 / -	%	ISO 527-1/-2
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	19 / -	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	14 / -	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	262 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	70 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	192 / *	°C	ISO 75-1/-2

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1100 / -	kg/m³	ISO 1183

CharacteristicsProcessingInjection MoldingRegional AvailabilityNorth AmericaOther text informationInjection moldingNylon 66 materials must be properly dried in order to provide parts Nylon 66 materials are For unopened bag/box, dry at 140F (60C) forFor material exposed to the atmosphere, if additional 04 - 0.20%.35 MPa (0 – 50 psi)Packing pressure affects It should be applied and maintained DisclaimerCopyright M-Base .