Zytel® 70G30HSLR BK099|PA66-GF30|DuPont物性表报告及物性特性介绍,Zytel® 70G30HSLR BK099|PA66-GF30|DuPont注塑参数详情-塑料物性表查询网

加工/物理特性	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
密度(Density) (73°F)	1370	kg/m³	ASTM D 792

流变性能(Rheological properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据
成型收缩(Molding shrinkage) (parallel)	0.3 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.0 / *	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	10000 / 7200	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	195 / 130	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3 / 5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	75 / -	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	12 / 14	kJ/m²	ISO 179/1eA
悬臂梁式冲击切口 (23°C)	12 / 14	kJ/m²	ISO 180/1A
ASTM数据(ASTM Data)
抗拉强度(Tensile Strength)	180	MPa	ASTM D 638
断裂伸长率(Elongation at Break)	3	%	ASTM D 638
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	8275	MPa	ASTM D 790
悬臂梁式冲击切口 (1/8 in)	0.11	kJ/m	ASTM D 256

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据
熔化温度(熔化温度(Melting temperature)) (10°C/min)	262 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	253 / *	°C	ISO 75-1/-2
Burning behav. at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5 / *	mm	IEC 60695-11-10
燃烧性厚度(Burning behav. at thickness h)	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8 / *	mm	IEC 60695-11-10
ASTM数据(ASTM Data)
UL 94 阻燃等级(Flame rating)	HB	-	UL 94
厚度测试(Thickness tested)	1.5	mm	-
DTUL @ 264 psi	248	°C	ASTM D 648
熔化温度(Melting 温度(Temperature))	263	°C	ASTM D 3418

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据
密度(Density)	1370 / -	kg/m³	ISO 1183

CharacteristicsProcessingInjection Molding, Blow MoldingDelivery formPellets, BlackSpecial CharacteristicsHeat stabilized or stable to heatFeaturesCreep Resistance, Fatigue Resistance, Thermal StabilityChemical ResistanceGeneral Chemical Resistance, Grease Resistance, Hydrolytically Stable, Oil ResistanceApplicationsAutomotive, .