Product TextsPBT, reinforced8	%	ISO 527-1/-2
Tensile creep modulus (1h)	4400	MPa	ISO 899-1
Tensile creep modulus (1000h)	2800	MPa	ISO 899-1
简支梁冲击强度(Charpy impact strength) (+23°C)	50	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	45	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	7	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	6	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	224	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	205	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	215	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	55	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	120	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8	mm	IEC 60695-11-10

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (1MHz)	3.6	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	190	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
电气强度(Electric strength)	28	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	500	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.45	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.18	%	Sim. to ISO 62
密度(Density)	1370	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	240	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724

CharacteristicsProcessingInjection MoldingDelivery formPelletsRegional AvailabilityEuropeOther text informationInjection moldingPREPROCESSING Water Content0,04% ISO 1817 Liquid F) (23°C)[/td][/tr][tr][td]Salt solutions[/td][/tr][tr][td] .