Crastin® HR5315HF BK503|PBT-GF15|DuPont物性表报告及物性特性介绍,Crastin® HR5315HF BK503|PBT-GF15|DuPont注塑参数详情-塑料物性表查询网

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
成型收缩(Molding shrinkage) (parallel)	0.5	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.1	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	5200	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	92	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	50	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	10	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	6	kJ/m²	ISO 179/1eA
弯曲弹性模量(Flexural modulus) (23°C)	4700	MPa	ISO 178
悬臂梁式冲击切口 (23°C)	10	kJ/m²	ISO 180/1A
悬臂梁式冲击切口	6	kJ/m²	ISO 180/1A
温度(Temperature)	-40	°C	ISO 180/1A
悬臂梁式冲击无切口(Izod Impact unnotched) (23°C)	40	kJ/m²	ISO 180/1U
洛氏硬度(Rockwell hardness)	R 117	-	ISO 2039-2

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
熔化温度(熔化温度(Melting temperature)) (10°C/min)	225	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	200	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	220	°C	ISO 75-1/-2
Oxygen index	20	%	ISO 4589-1/-2

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
相对介电常数(Relative permittivity) (1MHz)	3.7	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	150	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
相比漏电起痕指数(Comparative tracking index)	325	-	IEC 60112
ASTM数据(ASTM Data)
绝缘强度(Dielectric Strength) (Short Time)	25.3	kV/mm	ASTM D 149

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
吸水率(Water absorption)	0.08	%	Sim. to ISO 62
密度(Density)	1370	kg/m³	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formPellets, BlackAdditivesLubricantsChemical ResistanceGeneral Chemical Resistance, Hydrolytically StableApplicationsAutomotive, Asia Pacific, South and Central America, Near East/AfricaDisclaimerCopyright M-Base .