PB80 NL TD 21|(PBT+PC)|Melos物性表报告及物性特性介绍,PB80 NL TD 21|(PBT+PC)|Melos注塑参数详情-塑料物性表查询网

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
成型收缩(Molding shrinkage) (parallel)	1.5	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.5	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	2100	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	45	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	20	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	14	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	10	kJ/m²	ISO 179/1eA
悬臂梁式冲击切口 (23°C)	12	kJ/m²	ISO 180/1A
悬臂梁式冲击切口	8	kJ/m²	ISO 180/1A
温度(Temperature)	-30	°C	ISO 180/1A

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
熔化温度(熔化温度(Melting temperature)) (10°C/min)	225	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	75	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	130	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	150	°C	ISO 306
燃烧性厚度(Burning behav. at thickness h)	V-0	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.2	mm	IEC 60695-11-10
ASTM数据(ASTM Data)
UL 94 阻燃等级(Flame rating)	V-0	-	UL 94
厚度测试(Thickness tested)	1.6	mm	-

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	1E14	Ohm	IEC 60093
相比漏电起痕指数(Comparative tracking index)	225	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
吸水率(Water absorption)	0.4	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.15	%	Sim. to ISO 62
密度(Density)	1340	kg/m³	ISO 1183

CharacteristicsSpecial CharacteristicsFlame retardant, High impact or impact modified, U.V. stabilized or stable to weatherFeaturesThermal StabilityChemical ResistanceGeneral Chemical ResistanceApplicationsElectrical and ElectronicalRegional AvailabilityEuropeDisclaimerCopyright M-Base .