SCHULADUR® A GF 30 HI|PBT-I-GF30|A. Schulman物性表报告及物性特性介绍,SCHULADUR® A GF 30 HI|PBT-I-GF30|A. Schulman注塑参数详情-塑料物性表查询网

Schulman Product Texts30% glass fibre reinforced impact modified PBT16

ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	8400	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	110	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3.5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	66	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	12	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	230	°C	ISO 11357-1/-3
玻璃化转变温度(Glass transition temperature) (10°C/min)	22	°C	ISO 11357-1/-2
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	204	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	213	°C	ISO 75-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5	mm	IEC 60695-11-10

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	3.9	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	3.79	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	0.0019	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	0.0226	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
电气强度(Electric strength)	18.7	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	450	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1490	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Processing conditions acc. ISO	7790	-	ISO ....-2
Injection Molding, melt temperature	260	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	250	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

CharacteristicsProcessingInjection MoldingDelivery formGranulesAdditivesRelease agent, PlasticizerSpecial CharacteristicsHigh impact or impact modifiedRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSINGPretreatment .