SCHULADUR® A GF 15 HF FR 1|PBT-GF15 FR|A. Schulman物性表报告及物性特性介绍,SCHULADUR® A GF 15 HF FR 1|PBT-GF15 FR|A. Schulman注塑参数详情-塑料物性表查询网

Schulman Product TextsEasy flow 15% glass fibre reinforced flame retardant PBT with halogenated agent; without PBDE5	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	4	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	230	°C	ISO 11357-1/-3
玻璃化转变温度(Glass transition temperature) (10°C/min)	22	°C	ISO 11357-1/-2
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	180	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	211	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	201	°C	ISO 306
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	V-0	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	V-0	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.7	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). 5V at thickness h	5VA	class	IEC 60695-11-20
厚度测试(Thickness tested)	1.5	mm	IEC 60695-11-20
Oxygen index	28.5	%	ISO 4589-1/-2

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
相比漏电起痕指数(Comparative tracking index)	225	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1520	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Processing conditions acc. ISO	7790	-	ISO ....-2
Injection Molding, melt temperature	260	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	250	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

CharacteristicsProcessingInjection MoldingDelivery formGranulesAdditivesRelease agentSpecial CharacteristicsFlame retardantRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSINGPretreatment .