VESTODUR® 3030 nc (nf)|PBT|Evonik Industries物性表报告及物性特性介绍,VESTODUR® 3030 nc (nf)|PBT|Evonik Industries注塑参数详情-塑料物性表查询网

Product TextsVESTODUR® 3030 ncThe resin is best suited for manufacturing stiff, smalldiameter g., for loose fiber optic buffer tubes.16

ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	2600	MPa	ISO 527-1/-2
屈服应力(Yield stress)	55	MPa	ISO 527-1/-2
屈服应变(Yield strain)	9	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	>50	%	ISO 527-1/-2
Tensile creep modulus (1h)	2600	MPa	ISO 899-1
Tensile creep modulus (1000h)	1500	MPa	ISO 899-1
简支梁冲击强度(Charpy impact strength) (+23°C)	N	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	300	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	7	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	6	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	223	°C	ISO 11357-1/-3
玻璃化转变温度(Glass transition temperature) (10°C/min)	45	°C	ISO 11357-1/-2
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	55	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	135	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	180	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	110	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	110	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6	mm	IEC 60695-11-10

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	3.3	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	3.5	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	20	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	230	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	1E13	Ohm	IEC 60093
电气强度(Electric strength)	27	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	600	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.45	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.15	%	Sim. to ISO 62
密度(Density)	1310	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Processing conditions acc. ISO	7790	-	ISO ....-2
Injection Molding, melt temperature	260	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

CharacteristicsProcessingFilm Extrusion, Profile Extrusion, Sheet Extrusion, Other ExtrusionDelivery formPelletsSpecial CharacteristicsLight stabilized or stable to light, U.V. stabilized or stable to weatherRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationFilm extrusionPREPROCESSING INFORMATION05 % The drying time is dependent onWe recommend a drying time of approximately 5 hours at a temperature of 120°C 05 % The drying time is dependentWe recommend a drying time of approximately 5 hours at a temperature of 05 % The drying time is dependentWe recommend a drying time of approximately 5 hours at a temperature of 05 % The drying time is dependentWe recommend a drying time of approximately 5 hours at a temperature ofISO 1817 Liquid C) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid F) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid F) (90°C)[/td][/tr][tr][td]Salt solutions[/td][/tr][tr][td] .