VESTODUR® X9400 nc (nf)|PBT-GF10|Evonik Industries物性表报告及物性特性介绍,VESTODUR® X9400 nc (nf)|PBT-GF10|Evonik Industries注塑参数详情-塑料物性表查询网

Product TextsVESTODUR® X9400 ncThe compound is suitable for parts that are subjectedCompared with commonly used glass fiber reinforced PBT compounds 3	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	0.4	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	4500	MPa	ISO 527-1/-2
屈服应力(Yield stress)	90	MPa	ISO 527-1/-2
屈服应变(Yield strain)	4	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	5.5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	45	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	45	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	5	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	5	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	110	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	200	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	30	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	40	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6	mm	IEC 60695-11-10

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1350	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Processing conditions acc. ISO	7790	-	ISO ....-2
Injection Molding, melt temperature	260	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

CharacteristicsProcessingInjection MoldingDelivery formPelletsSpecial CharacteristicsHeat stabilized or stable to heatRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSING INFORMATION05 % The drying time is dependentWe recommend a drying time of approximately 5 hours at a temperature ofISO 1817 Liquid C) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid F) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid F) (90°C)[/td][/tr][tr][td]Salt solutions[/td][/tr][tr][td] .