VESTODUR® X9417 blk (sw) E70286|PBT-GF15|Evonik Industries物性表报告及物性特性介绍,VESTODUR® X9417 blk (sw) E70286|PBT-GF15|Evonik Industries注塑参数详情-塑料物性表查询网

Product TextsVESTODUR® X9417 blk E70286 The compound is suitable for parts that are sub- Compared with commonly used glass fiber rein-4	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.5	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	6000	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	100	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	2.6	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	25	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	25	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	5	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	5	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	190	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	215	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	205	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	70	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	100	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8	mm	IEC 60695-11-10

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	4	-	IEC 60250
体积电阻率(Volume resistivity)	1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	1E14	Ohm	IEC 60093
电气强度(Electric strength)	27	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	325	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.5	%	Sim. to ISO 62
密度(Density)	1450	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Processing conditions acc. ISO	7790	-	ISO ....-2
Injection Molding, melt temperature	260	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

CharacteristicsProcessingInjection MoldingDelivery formPelletsSpecial CharacteristicsHeat stabilized or stable to heatRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSING INFORMATION05 % The drying time is dependentWe recommend a drying time of approximately 5 hours at a temperature ofISO 1817 Liquid C) (23°C)[/td][/tr][tr][td] ISO 1817 Liquid F) (23°C)[/td][/tr][tr][td]Salt solutions[/td][/tr][tr][td] .