POLYFORT® FIPP 20 T LE K1832|PP-T20|A. Schulman物性表报告及物性特性介绍,POLYFORT® FIPP 20 T LE K1832|PP-T20|A. Schulman注塑参数详情-塑料物性表查询网

Schulman Product Texts20% talc filled low emission PP copolymer compound with increased impact strength for automotive interiorparts (VW TL 52388-B); increased scratch resistance16

ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	1500	MPa	ISO 527-1/-2
屈服应力(Yield stress)	21	MPa	ISO 527-1/-2
屈服应变(Yield strain)	5	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	>50	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	10	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	48	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	103	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	80	E-6/K	ISO 11359-1/-2

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	2.8	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	2.8	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	20	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	10	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	>1E15	Ohm	IEC 60093

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.04	%	Sim. to ISO 62
密度(Density)	1050	kg/m³	ISO 1183

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体热导率(Thermal conductivity of melt)	0.38	W/(m K)	-
规格的热容融化(Spec. heat capacity of melt)	1520	J/(kg K)	-
Eff. thermal diffusivity	2.60E-7	m²/s	-
喷射温度(Ejection temperature)	100	°C	-

CharacteristicsProcessingInjection MoldingDelivery formGranulesAdditivesRelease agentRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSINGPretreatment .