Cardia Biohybrid H-M01|(PSAC+PP)|Cardia Bioplastics

Product TextsDescription This grade of resin is compatibilised to offer a high level of mechanical strength, good impact resistance and toughness. The resin is based on corn starch which is a renewable material. This resin is suitable for a wide range of products manufactured by injection moulding or extrusion processes. Due to its content of polypropylene the material is not a fully biodegradable polymer and it is not intended for ultimate disposal in commercial composting facilities. If biodegradability or compostability is required, use of Cardia Compostable B-M or TBM resin is recommended.9	g/10min	ASTM D 1238
温度(Temperature)	190	°C	-
负载(Load)	2.16	kg	-
模具收缩(Mold Shrinkage) (MD)	0.01	mm/mm	ASTM D 955
密度(Density) (73°F)	1070	kg/m³	ASTM D 792

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
抗拉强度(Tensile Strength) at Break	15	MPa	ASTM D 638
断裂伸长率(Elongation at Break)	16	%	ASTM D 638

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
熔化温度(Melting 温度(Temperature))	157	°C	ASTM D 3418

CharacteristicsProcessingInjection Molding, Other ExtrusionEcological valuationContains renewable resourcesRegional AvailabilityNorth America, Europe, .
[/td][/tr][/table]

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/wuxingbiao/show-85961.html

免责声明: 本文 Cardia Biohybrid H-M01|(PSAC+PP)|Cardia Bioplastics 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络