FORTRON 0317|PPS|Ticona物性表报告及物性特性介绍,FORTRON 0317|PPS|Ticona注塑参数详情-塑料物性表查询网

Product Texts0317 exhibits a high melt strength for extrusion processes. TheTheAvailable standard in powder (0317B1), pellet (0317B1) and

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
破坏时应变(Stress at break)	90	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	8	%	ISO 527-1/-2

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	275	°C	ISO 11357-1/-3
玻璃化转变温度(Glass transition temperature) (10°C/min)	90	°C	ISO 11357-1/-2
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	115	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (8.00 MPa)	95	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	52	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	53	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at thickness h	V-0	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.0	mm	IEC 60695-11-10

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (1MHz)	4.6	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	11	E-4	IEC 60250
体积电阻率(Volume resistivity)	1E9	Ohm*m	IEC 60093
电气强度(Electric strength)	18	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	125	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.02	%	Sim. to ISO 62
密度(Density)	1350	kg/m³	ISO 1183

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
规格的热容融化(Spec. heat capacity of melt)	1830	J/(kg K)	-

CharacteristicsProcessingInjection Molding, Film Extrusion, Profile Extrusion, Sheet Extrusion, Other ExtrusionDelivery formPellets, PowderRegional AvailabilityNorth America, Europe, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSING Predrying in a dehumidified air dryer at 120 degC/3-4 hoursA All mold cavities must .