Thermocomp MH0500C|PP-X|SABIC_IP物性表报告及物性特性介绍,Thermocomp MH0500C|PP-X|SABIC

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
成型收缩(Molding shrinkage) (parallel)	1.6	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.5	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	2920	MPa	ISO 527-1/-2
屈服应力(Yield stress)	19	MPa	ISO 527-1/-2
屈服应变(Yield strain)	3.3	%	ISO 527-1/-2
破坏时应变(Stress at break)	19	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	13.6	%	ISO 527-1/-2
弯曲弹性模量(Flexural modulus) (23°C)	2900	MPa	ISO 178
悬臂梁式冲击切口 (23°C)	4	kJ/m²	ISO 180/1A
悬臂梁式冲击无切口(Izod Impact unnotched) (23°C)	12	kJ/m²	ISO 180/1U
ASTM数据(ASTM Data)
拉伸模量(Tensile Modulus)	4130	MPa	ASTM D 638
抗拉强度(Tensile Strength) at Yield	18	MPa	ASTM D 638
抗拉强度(Tensile Strength) at Break	16	MPa	ASTM D 638
屈服伸长率(Elongation at Yield)	3.2	%	ASTM D 638
断裂伸长率(Elongation at Break)	19.5	%	ASTM D 638
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	2060	MPa	ASTM D 790
悬臂梁式冲击切口 (1/8 in)	0.048	kJ/m	ASTM D 256

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	82	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	122	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	61	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	64	E-6/K	ISO 11359-1/-2
ASTM数据(ASTM Data)
热膨胀系数(Coefficient of Thermal Expansion) (MD)	61.2	E-6/K	ASTM D 696
热膨胀系数(Coefficient of Thermal Expansion) (TD)	63	E-6/K	ASTM D 696
DTUL @ 66 psi	126	°C	ASTM D 648
DTUL @ 264 psi	80	°C	ASTM D 648

CharacteristicsProcessingInjection MoldingRegional AvailabilityNorth America, Asia Pacific, South and Central AmericaDisclaimerCopyright M-Base .