Akulon® Ultraflow K-FKMV5 /C|PA6-MD25|DSM物性表报告及物性特性介绍,Akulon® Ultraflow K-FKMV5 /C|PA6-MD25|DSM注塑参数详情-塑料物性表查询网

Product Texts25% Mineral Reinforced, Flame Retardant (Halogen free), High Flow16 / *	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	0.6 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	0.8 / *	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	6200 / -	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	65 / -	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	1.8 / -	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	25 / 20	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	2 / 2	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	110 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	205 / *	°C	ISO 75-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	V-2 / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5 / *	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	V-2 / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8 / *	mm	IEC 60695-11-10

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
体积电阻率(Volume resistivity)	>1E13 / -	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	* / >1E15	Ohm	IEC 60093
相比漏电起痕指数(Comparative tracking index)	* / 600	-	IEC 60112

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	6.2 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	1.8 / *	%	Sim. to ISO 62
密度(Density)	1380 / -	kg/m³	ISO 1183

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density) of melt	1170	kg/m³	-
熔体热导率(Thermal conductivity of melt)	0.201	W/(m K)	-
规格的热容融化(Spec. heat capacity of melt)	2250	J/(kg K)	-
Eff. thermal diffusivity	7.63E-8	m²/s	-

CharacteristicsProcessingInjection MoldingDelivery formPelletsAdditivesRelease agentSpecial CharacteristicsHeat stabilized or stable to heatRegional AvailabilityEuropeOther text informationInjection moldingInjection Molding RecommendationsDisclaimerCopyright M-Base .