Durethan® BKV 50 H2.0 EF|PA6-GF50|LANXESS物性表报告及物性特性介绍,Durethan® BKV 50 H2.0 EF|PA6-GF50|LANXESS注塑参数详情-塑料物性表查询网

0 EF | PA6-GF50 |LANXESS Product TextsPA 6, 50 % glass fibres, injection moulding, improved flowability, heat-ageing stabilized

流变性能(Rheological properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	23 / *	cm³/10min	ISO 1133
温度(Temperature)	270 / *	°C	ISO 1133
负载(Load)	5 / *	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	0.2 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	0.5 / *	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	16000 / -	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	210 / -	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	2.5 / -	%	ISO 527-1/-2

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	222 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	210 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	220 / *	°C	ISO 75-1/-2

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1570 / -	kg/m³	ISO 1183

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density) of melt	1340	kg/m³	-
熔体热导率(Thermal conductivity of melt)	0.285	W/(m K)	-
规格的热容融化(Spec. heat capacity of melt)	1770	J/(kg K)	-
Eff. thermal diffusivity	1.21E-7	m²/s	-
喷射温度(Ejection temperature)	140	°C	-

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	290	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724

CharacteristicsProcessingInjection MoldingDelivery formPelletsAdditivesRelease agentRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSING Water content: 0.1 % .