0 | PA6-GF50 |LANXESS Product TextsPA 6, injection molding grade, 50 % glass fibres, good heat-ageing resistance

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	14500 / 9500	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	220 / 140	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3 / 5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	100 / 110	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	90 / 85	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	20 / 25	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	15 / 15	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	222 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	205 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	215 / *	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	200 / *	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	20 / *	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	70 / *	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	5 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	1.5 / *	%	Sim. to ISO 62
密度(Density)	1570 / -	kg/m³	ISO 1183

材料特殊性能(Material specific properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
粘数(Viscosity number)	140 / *	cm³/g	ISO 307, 1157, 1628

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	290	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724

CharacteristicsProcessingInjection MoldingDelivery formPelletsAdditivesRelease agentSpecial CharacteristicsHeat stabilized or stable to heatRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSING Water content: 0.1 % .